There are different types of stainless steels: when nickel is added, for instance, the austenite structure of iron is stabilized. This crystal structure makes such steels non-magnetic and less brittle at low temperatures. For higher hardness and strength, carbon is added to produce high grade stainless steel. When subjected to adequate heat treatment these steels are used as razor blades, cutlery, tools etc.
Significant quantities of manganese have been used in many stainless steel compositions. Manganese preserves an austenitic structure in the steel as does nickel, but at a lower cost.
Stainless steels are also classified by their crystalline structure:
- Austenitic, or 300 series, stainless steels comprise over 70% of total stainless steel production. They contain a maximum of 0.15% carbon, a minimum of 16% chromium and sufficient nickel and/or manganese to retain an austenitic structure at all temperatures from the cryogenic region to the melting point of the alloy. A typical composition of 18% chromium and 10% nickel, commonly known as 18/10 stainless is often used in flatware. Similarly 18/0 and 18/8 is also available. “Superaustenitic” stainless steels, such as alloy AL-6XN and 254SMO, exhibit great resistance to chloride pitting and crevice corrosion due to high Molybdenum contents (>6%) and nitrogen additions and the higher nickel content ensures better resistance to stress-corrosion cracking over the 300 series. The higher alloy content of "Superaustenitic" steels means they are fearsomely expensive and similar performance can usually be achieved using duplex steels at much lower cost.
- Ferritic stainless steels are highly corrosion resistant, but less durable than austenitic grades. They contain between 10.5% and 27% chromium and very little nickel, if any. Most compositions include molybdenum; some, aluminium or titanium. Common ferritic grades include 18Cr-2Mo, 26Cr-1Mo, 29Cr-4Mo, and 29Cr-4Mo-2Ni .
- Martensitic stainless steels are not as corrosion resistant as the other two classes, but are extremely strong and tough as well as highly machineable, and can be hardened by heat treatment. Martensitic stainless steel contains chromium (12-14%), molybdenum (0.2-1%), zero to less than 2% nickel, and about 0.1-1% carbon (giving it more hardness but making the material a bit more brittle). It is quenched and magnetic. It is also known as "series-00" steel.
- Precipitation-hardening martensitic stainless steels have corrosion resistance comparable to austenitic varieties, but can be precipitation hardened to even higher strengths than the other martensitic grades. The most common, 17-4PH, uses about 17% chromium and 4% nickel. There is a rising trend in defence budgets to opt for an ultra-high-strength stainless steel if possible in new projects as it is estimated that 2% of the US GDP is spent dealing with corrosion. The Lockheed-Martin JSF is the first aircraft to use a precipitation hardenable stainless steel - Carpenter Custom 465 - in its airframe.
- Duplex stainless steels have a mixed microstructure of austenite and ferrite, the aim being to produce a 50:50 mix although in commercial alloys the mix may be 40:60 respectively. Duplex steel have improved strength over austenitic stainless steels and also improved resistance to localised corrosion particularly pitting, crevice corrosion and stress corrosion cracking. They are characterised by high chromium (19-28%) and molybdenum (up to 5%) and lower nickel contents than austenitic stainless steels.
Please contact Mark Heffernan for a full list of high grade stainless steel products or download our product listing here. |